The authors investigate the mechanism of lattice thermal conductivity ($\kappa_{\text{lat}}$) reduction across p-type (Mn) and n-type (Co, Ir) doped $\beta$-FeSi$_2$ by correlating thermal transport measurements with structural and vibrational probes. Overcoming the limits of conventional mass- and size-mismatch phonon scattering, they reveal that dopant-induced lattice softening fundamentally weakens interatomic force constants. Remarkably, Co doping yields a ~71% reduction in $\kappa_{\text{lat}}$ at 300 K despite negligible mass contrast, driven by lowered phonon group velocities and amplified anharmonic scattering.
Mass and size mismatches are not required to slash thermal conductivity: dopant-induced lattice softening alone drives a 71% collapse in $\beta$-FeSi$_2$'s $\kappa_{\text{lat}}$ by weakening atomic force constants.
Suppressing lattice thermal conductivity (\k{appa}lat) is pivotal for thermoelectric efficiency. While traditional strategies rely heavily on phonon scattering from mass- and size-mismatches, we demonstrate a robust \k{appa}lat suppression mechanism driven by dopant-induced lattice stiffness modulation. Through a comparative analysis of p-type (Mn) and n-type (Co, Ir) doping in the \b{eta}-FeSi2 model system, we show that Co and Ir doping significantly reduce \k{appa}lat. Notably, Co doping achieves a ~71% reduction at 300 K even without significant mass and size contrast. By correlating transport data with neutron powder diffraction, heat capacity, and Raman spectroscopy, we reveal anomalous lattice expansion, a substantial reduction in Debye temperature, and marked vibrational redshift and broadening. These systematic changes provide strong evidence for atomic-scale lattice softening and a fundamental weakening of interatomic force constants, which synergistically lower phonon group velocities and amplify anharmonic scattering. Our findings establish lattice stiffness manipulation as a powerful strategy for thermal management, offering a distinct design pathway beyond traditional mass- and strain-fluctuation models.