The authors evaluated the electrothermal hot-spot dynamics and retrapping behavior of native titanium nitride superconducting nanowires embedded directly in the front-end-of-line of a commercial 22 nm FD-SOI process across temperatures from 0.15 to 1.19 K. Quantifying heat dissipation in these buried films is essential to determining whether foundry CMOS can monolithically support bistable superconducting detectors and high-kinetic-inductance memory. The devices exhibited strong electrothermal hysteresis ($I_{\mathrm{sw}}/I_{\mathrm{r}} \approx 7.4\text{--}9.8$) dominated by an unexpectedly weak interfacial phonon cooling channel ($\Sigma_K \approx 7.9 \text{ W}/(\text{m}^2 \text{K}^4)$), establishing a geometric crossover length of $\ell^* \approx 3.5\ \mu\text{m}$ between longitudinal and transverse dissipation.
Commercial 22 nm CMOS can natively host hysteretic superconducting nanowires without the dense back-end metallization quenching normal hot spots, clearing a path for standard silicon foundries to manufacture monolithic cryo-electronic detectors and memories.
Superconducting films native to a commercial CMOS process enable co-integration of superconducting devices (high-kinetic-inductance elements and nanowire detectors) with cryogenic CMOS on one monolithic die. Such films are buried in the front-end-of-line, beneath the back-end-of-line metal stack, an environment that might quench a self-heated hot spot. Current-voltage characteristics are reported for titanium nitride (TiN) nanowires in the polycrystalline-silicon resistor layer of a 22 nm FD-SOI process, and measured retrapping currents are compared with thermal models for longitudinal conduction to the contacts and interfacial phonon cooling into the stack. The wires are strongly hysteretic, with switching-to-retrapping current ratios I_sw/I_r of 7.4-9.8, sustaining a normal hot spot. For two wires of length ell = 50 micrometers and widths W = 0.50 and 1.00 micrometers, over bath temperatures T_b = 0.15-1.19 K, I_r follows the interfacial form (T_hs^n - T_b^n)^(1/2) with n = 4 (T_hs, the effective hot-spot temperature), and is strongly inconsistent with the (T_hs - T_b)^(1/2) constant-kappa longitudinal-conduction limit; free-exponent fits give n = approximately 4.8-5.0. An effective cooling coefficient Sigma_K = 7.9(3) W/(m^2 K^4) describes the data: 31(21) times below the acoustic- (diffuse-) mismatch value for a single clean interface, and approximately 12 times below the lowest previously reported comparable nanowire coefficient. The model-based film thermal conductivity is kappa = approximately 20 mW/(m K). Across lengths ell = 1-50 micrometers, I_r matches neither ell^(-1) of pure longitudinal conduction nor ell^0 of pure interfacial cooling; a two-channel model reproduces I_r(ell) with crossover length ell* = approximately 3.5 micrometers predicted, to an O(1) prefactor, from Sigma_K and kappa.