This study reports the experimental synthesis of Mg2RhH6, a superconducting hydride achieved at a significantly reduced pressure of 30 GPa, marking a notable advancement in the quest for high critical temperature superconductors. The synthesis involves a two-step process, first creating a precursor Mg2RhH5 followed by hydrogen supplementation that facilitates a structural transition and electron filling in anti-bonding orbitals. The resulting superconductor exhibits a critical temperature (Tc) of 24 K at 30 GPa, increasing to 29 K at 53 GPa, demonstrating thermodynamic stability and potential for further exploration in the field of superconductivity.
Achieving superconductivity in Mg2RhH6 at just 30 GPa opens new avenues for discovering high-temperature superconductors without extreme pressure requirements.
Although tremendous progress has been made in recent years in the field of polyhydride superconductors, the realization of high critical temperature superconductivity still relies on formidable high pressures. Searching for superconducting hydrides at lower pressures is of particular importance. Here we report the first experimental synthesis of the Mg2RhH6, which achieves superconductivity under a significantly reduced pressure of 30 GPa. The synthesis of Mg2RhH6 proceeds via a two step process (1) preparation of the Mg2RhH5 precursor containing hydrogen atoms stabilized by covalent bonding, followed by (2) hydrogen supplementation resulting in the filling of electrons into anti bonding orbitals above 30 GPa, which was accompanied by the structural transition from RhH5 square pyramid to RhH6 octahedron. Superconductivity is achieved at 30 GPa with a Tc of 24 K, which is further enhanced to 29 K at 53 GPa, evidenced by a sharp drop of resistivity to zero and characteristic suppression of Tc under applied magnetic fields. Our experiments prove the Mg2RhH6 superconductor to be thermodynamically stable above 30 GPa, making it the first case exhibiting a Tc of approximately 30 K at a readily accessible pressure. This study pioneers a highly promising pathway for the rational design and discovery of high temperature superconductors within phonon mediated BCS framework.