This study investigates the high-pressure behavior of β'-Mn3(PO4)2 using synchrotron X-ray diffraction and density-functional theory, revealing that the material undergoes irreversible structural disorder beyond 14.1 GPa. The research identifies that this disorder is linked to the loss of long-range crystallographic order and is maintained even after returning to ambient pressure. Key findings include the mechanical instability of the crystalline phase near the transition pressure and the distinct compressibility behaviors of Mn-O polyhedra versus rigid PO4 tetrahedra, which together illuminate the complex response of phosphate frameworks under pressure.
Irreversible structural disorder in β'-Mn3(PO4)2 emerges under pressure, challenging our understanding of phase stability in complex materials.
The high-pressure structural behavior of β'-Mn3(PO4)2 was investigated using synchrotron X-ray diffraction up to 20 GPa combined with density-functional theory calculations. At ambient conditions, β'-Mn3(PO4)2 crystallizes in a monoclinic structure that exhibits strongly anisotropic compression. The pressure dependence of the unit-cell volume was described using a third-order Birch-Murnaghan equation of state, and the principal axes of compressibility were determined. Above 14.1 GPa, significant broadening and weakening of the diffraction peaks are attributed to the onset of irreversible pressure-induced structural disorder associated with the loss of long-range crystallographic order. The disordered state persists after decompression to ambient pressure, demonstrating the irreversible nature of the transformation. The calculations accurately reproduce the experimental compressional behavior and provide insights into the microscopic structural evolution under pressure. Compression is mainly accommodated through distortions of the Mn-O polyhedra, whereas the PO4 tetrahedra behave as comparatively rigid units. Several initially penta-coordinated Mn sites progressively evolve toward octahedral coordination under compression, while selected MnO6 polyhedra exhibit anomalous distortions and elastic softening preceding the onset of disorder. Elastic constant calculations further reveal that the crystalline phase becomes mechanically unstable near the experimentally observed transition pressure. The combined experimental and computational results suggest that the high-pressure response of β'-Mn3(PO4)2 is influenced by the interplay between framework complexity, anisotropic polyhedral compressibility, and elastic instability, providing new insight into pressure-induced structural degradation in structurally complex phosphate frameworks.