This study developed a high-sensitivity hydrogen gas permeation system capable of operating at pressures up to 50 bar and temperatures up to 250°C, enabling precise quantification of hydrogen-material interactions. Through systematic analysis of surface conditions and testing variables, it was found that surface oxides significantly hinder hydrogen permeation at room temperature, necessitating oxide removal for measurable uptake. The results reveal that under optimized conditions, hydrogen transport aligns with bulk diffusion-controlled behavior, adhering to Sieverts' law and exhibiting Arrhenius characteristics for diffusivity and permeability across a temperature range of 25 to 150°C.
Surface oxides can completely suppress hydrogen uptake, revealing critical insights into hydrogen-material interactions that could reshape industrial applications.
There is a need to develop quantitative, high-resolution hydrogen gas (H2) permeation techniques to provide a better understanding of hydrogen-material interactions. This study aims to develop and validate a high-sensitivity H2 permeation system, which is then leveraged to systematically quantify the influence of surface condition and key testing variables (surface oxides, residual gas impurities, pressure, and temperature) on hydrogen permeation. A gas permeation system capable of operating at pressures up to 50 bar and temperatures up to 250 C was developed, incorporating high-sensitivity mass spectrometric detection and controlled surface preparation protocols. Permeation transients were analysed in a model material (annealed pure Fe) to determine hydrogen diffusivity and permeability under systematically varied surface states, oxygen contents, pressures and temperatures. Surface oxides are shown to play a dominant role in controlling hydrogen permeation at room temperature. The presence of oxide layers can severely hinder or completely suppress hydrogen uptake, with measurable permeation requiring oxide removal via pickling and Pd coating on both surfaces, or activation through hydrogen-assisted reduction at elevated temperature. Residual oxygen present prior to hydrogen exposure further reduces permeability by modifying surface boundary conditions, indicating strongly surface-controlled kinetics. Under optimised surface conditions, hydrogen transport follows bulk diffusion-controlled behaviour, with steady-state flux obeying Sieverts' law at 25 C (1-5 bar) and diffusivity and permeability exhibiting Arrhenius behaviour between 25 and 150 C at 5 bar, indicating bulk diffusion-controlled transport. The developed system resolves hydrogen fluxes as low as 1.98x10-9 mol(m2 s) and provides a robust platform for investigating surface, mechanical and environmental effects on H2 permeation.