The study investigates the high-pressure behavior of two rare-earth oxides, (CePr)O2 – δ and (CePrLa)O2 – δ, with varying configurational entropy using synchrotron X-ray diffraction and Raman spectroscopy. Both oxides maintain a cubic fluorite structure up to 30 GPa, but exhibit an anomaly between 9-16 GPa linked to lattice distortions and bond angle bending. Increased cationic disorder in (CePrLa)O2−δ leads to amorphization above 22 GPa, revealing a connection between configurational entropy and structural stability under pressure.
High-entropy oxides can withstand extreme pressures, but only up to a point: beyond that, their very disorder makes them fall apart.
We report a comparative high-pressure study of two fluorite-type rare-earth oxides with increasing configurational entropy, (CePr)O2 – δ and (CePrLa)O2 – δ. Synchrotron-based powder X-ray diffraction and Raman spectroscopy were carried out up to 30 and 20 GPa, respectively. Both compounds retain the cubic fluorite structure throughout the pressure range explored, although an anomaly is observed between 9 and 16 GPa, characterized by a compressibility plateau and changes in vibrational modes. This behavior is attributed to local lattice distortions and a progressive bond angle bending rather than abrupt phase transitions. In (CePrLa)O2−δ, the onset of amorphization is observed above 22 GPa, highlighting its reduced structural stability. The bulk modulus of both systems shows a slight decrease after the onset of the anomaly, suggesting subtle lattice softening. Raman spectroscopy reveals suppression of the F2g mode intensity with increasing cationic disorder, and under compression, partial reordering is evidenced by an increase in the RE–O mode intensity. Our results highlight the complex interplay between configurational entropy, cation size, and pressure in determining the structural stability and vibrational properties of rare-earth high-entropy oxides and provide insight into the mechanisms governing their resilience and local disorder under extreme conditions.