The study investigates the electrocatalytic activity of Zn-Al alloy electrodes with varying Al content for the oxygen evolution reaction (OER) in alkaline water splitting. Through electrochemical measurements and first-principles calculations, the researchers found that Zn-Al alloys with 10 wt.% Al (Zn$_{0.9}$Al$_{0.1}$) exhibited the best performance, showing a three-fold increase in anodic exchange current density and a significantly lower overpotential compared to pure Zn. This enhanced performance is attributed to a balance between thermodynamic stability, electronic structure, and the availability of reaction active sites.
A specific Zn-Al alloy (Zn$_{0.9}$Al$_{0.1}$) achieves OER performance rivaling transition-metal catalysts, offering a low-cost alternative for alkaline water splitting.
Electrochemical water electrolysis, which produces clean energy carriers to mitigate carbon emissions, lacks suitable, low-cost electrodes for efficient oxygen evolution reaction (OER) in alkaline water splitting. To address this challenge, we developed Zn-Al alloy electrodes with varying Al contents up to 20 wt.% via powder metallurgy method and conducted electrochemical measurements of the OER in alkaline solution to investigate their catalytic performance. We also performed first-principles calculations to examine their thermodynamic phase stability and electronic structures. Both theoretical and experimental results indicated that incorporating $\geq 20$ wt.% Al into Zn led to thermodynamic phase instability and secondary-phase segregation in Al-rich regions, limiting reaction kinetics and reducing catalytic efficiency. Although the Al content of 5 wt.% into Zn exhibited favorable thermodynamic and electronic characteristics, but its electrochemical performance was inefficient and poor due to inadequate reaction active sites on the surface. In contrast, the 10 wt.% and 15 wt.% Al into Zn showed approximately three- and two-fold increases in anodic exchange current density relative to pure Zn, respectively. Additionally, the anodic overpotential losses ($\eta_{0,a}$) measured at a current density of 12 mAcm$^{-2}$ were 0.240 V for Zn$_{0.9}$Al$_{0.1}$ and 0.5603 V for Zn$_{0.85}$Al$_{0.15}$, significantly lower than that of pure Zn ($\eta_{0,a} = 1.086$ V). While Zn$_{0.9}$Al$_{0.1}$ and Zn$_{0.85}$Al$_{0.15}$ showed similar charge transfer resistance ($R_{\rm CT}$), Zn$_{0.9}$Al$_{0.1}$ demonstrated superior reaction kinetics and lower $\eta_{0,a}$ across all samples tested. Furthermore, the improved kinetics and reduced overpotential of the Zn-Al alloys favorably compare with those of other transition-metal-based catalysts, including Fe-Co-Ni-Mo alloys and Fe-doped CuO.