This work investigates the thermodynamic driving forces behind halide segregation in mixed halide (Br-I) perovskites using first-principles calculations on slab models with varying halide distributions. The simulations reveal that bromide ions preferentially occupy surface sites over bulk sites, with a stronger segregation tendency observed in MAPb(Br$_x$I$_{1-x}$)$_3$ compared to FA$_{0.8}$Cs$_{0.2}$Pb(Br$_x$I$_{1-x}$)$_3$, indicating the A-site cation's influence. The study also identifies photo-generated holes localizing near iodide ions, accelerating iodide vacancy formation and promoting segregation.
Bromide ions in mixed halide perovskites have a surprising preference for surface sites over bulk, revealing a key thermodynamic driver of halide segregation.
Halide segregation in metal halide perovskites limits their bandgap tunability and hinders their adoption in tandem solar cells and light emitting diodes. Here, we reveal the thermodynamic driving force behind halide segregation in mixed halide (Br-I) perovskites. By performing first-principles calculations on slab models with varying bromide and iodide distributions, we demonstrate that bromide ions preferentially occupy surface sites over bulk sites. Our simulations show that the segregation tendency is higher in MAPb(Br$_x$I$_{1-x}$)$_3$ (MA=methylammonium) compared to FA$_{0.8}$Cs$_{0.2}$Pb(Br$_x$I$_{1-x}$)$_3$, highlighting the role of the A-site cation. To quantify this effect, we establish a descriptor for halide segregation: the difference in defect formation energies of Br antisite defects between the bulk and the surface, which confirms the role of the A-site cation at equimolar Br-I concentration. Furthermore, we identify the localization of photo-generated holes near iodide ions, which triggers their oxidation and accelerates the formation of iodide vacancies, thereby promoting segregation. Overall, this work establishes defect thermodynamics as a framework for understanding halide segregation and provides a structural basis for designing stable mixed halide perovskites.