Molecular dynamics simulations of collision cascades in pure W and a WTaCrV alloy, using machine-learning potentials, reveal that subcascade formation and the presence of lighter elements significantly influence defect nucleation. The WTaCrV alloy exhibits superior resistance to primary irradiation damage due to more frequent cascade splitting and the ability of Cr and V to absorb point defects, leading to fewer dislocations and the absence of voids compared to pure W. These findings highlight the role of alloy composition in mitigating irradiation-induced structural degradation.
Refractory alloys with lighter elements like Cr and V can suppress void formation and dislocation loops under irradiation by promoting cascade splitting and accommodating point defects.
Collision cascades and defect-formation mechanisms in pure W and the WTaCrV refractory high-entropy alloy were investigated using molecular dynamics simulations over primary knock-on atom (PKA) energies of 0.1-100 keV. Machine-learning tabulated Gaussian approximation potentials (tabGAP), complemented by short-range Ziegler-Biersack-Littmark (ZBL) interactions, were employed. Analysis of the heat spike lifetime, affected region, atomic relocations and surviving defects reveals an importance of subcascade formation and presence of light elements in the alloy. Cascade splitting into subcascades contributes to the distribution of the PKA energy over a larger region in the material, nucleating less dislocations and smaller voids - latter being present only in W and absent in WTaCrV. Since cascade splitting is more frequently observed in WTaCrV, the alloy shows better resistance to primary irradiation damage compared to pure W. Apart from cascade splitting, analysis of interstitials shows that Cr and to lesser extent V, being lighter and smaller elements, accommodate the damage in form of point defects, contributing to the mitigation of formation of the dislocation loops.