The authors synthesized lead-free BaZr0.2Ti0.8O3 ceramics via solid-state reaction and evaluated their uncharacterized pyroelectric behavior across polarized, depolarized, relaxed, and restored states. Resolving the polar nanoregion dynamics in these relaxor materials is critical for optimizing high-permittivity dielectrics for low-loss, tunable microelectronic components. Thermal-wave profiling and dielectric spectroscopy revealed a pronounced, field-history-dependent pyroelectric asymmetry across opposite sample surfaces, confirming the coexistence of non-ergodic relaxor polar nanoregions and ferroelectric states near room temperature.
Field-cycling history dictates severe spatial asymmetry in the pyroelectric response of BaZr0.2Ti0.8O3, proving that non-ergodic relaxor domains and ordered ferroelectric phases directly coexist at near-ambient temperatures.
BaxZr1-xTiO3 ceramics with 0.15<x<0.25, which have high dielectric permittivity, small leakage currents and low dissipation factor, are promising materials for tunable capacitor devices, multilayered ceramic capacitors and piezoelectric actuators. These materials reveal relaxor properties due to the local chemical strains caused by the isovalent substitution of Ti4+ ions by Zr4+ ions with a larger ionic size. However, to the best of our knowledge, the pyroelectric properties of BaxZr1-xTiO3 ceramics with x~0.2 have not been studied. To fill the gap in knowledge, we perform the pyroelectric thermo-wave probing of BaZr0.2Ti0.8O3 ceramics prepared by the solid-state synthesis. Results of the thermo-wave probing of the most interesting polar states, namely polarized, depolarized, relaxed and restored polarized states, reveal the pronounced pyroelectric response that can be strongly asymmetric with respect to the opposite surfaces of the ceramics. The asymmetry and profiles of pyroelectric response depend significantly on the pre-history of the electric field cycling indicating possible non-ergodic relaxor-type polar states in the ceramic sample. X-ray diffraction spectrum, recorded at room temperature, reveals the virtual absence of the macroscopic tetragonality and the weak asymmetry of the (200) peak, which indicate the small tetragonality inside the Ti-enriched polar nanoregions. Decrease of the relative intensity of the Raman band at 714 cm-1 occurring upon heating evidences the diffuse ferroelectric-paraelectric phase transition between 30 C and 40 C. The temperature dependence of the dielectric permittivity obeys modified Curie-Weiss law with power 1.4, indicating that both ordered ferroelectric and relaxor states coexist in the BaTi0.8Zr0.2O3 ceramics.