The authors evaluated the thermodynamic accessibility of 54 quaternary mixed-metal chalcohalides ($M\text{(II)}_2M\text{(III)}\text{Ch}_2\text{X}_3$) by coupling density functional theory with the Alexandria Materials Database and validating candidates through solution-phase processing. Although all 54 target compositions are strictly unstable with respect to the convex hull, a notable fraction reside within computational uncertainty limits and decompose along five predictable reaction pathways. Leveraging these near-hull thermodynamic insights, the team achieved the first experimental synthesis of the previously unreported semiconductor $\text{Sn}_2\text{InS}_2\text{Br}_3$ in a multiphase thin film.
Metastability is not a barrier to discovery: despite all 54 evaluated chalcohalides sitting above the convex hull, proximity-based screening successfully guided the first-ever synthesis of the novel semiconductor $\text{Sn}_2\text{InS}_2\text{Br}_3$.
Quaternary mixed-metal chalcohalides (MMCHs) are a promising mixed-anion semiconductor family, but their thermodynamic accessibility remains largely unexplored. We combine density functional theory with the Alexandria Materials Database to carry out a rapid and reliable evaluation of the thermodynamic accessibility of 54 M(II)$_2$M(III)Ch$_2$X$_3$ compounds. All evaluated MMCHs are predicted to be thermodynamically unstable, but a considerable fraction of MMCHs lie within computational uncertainty of the convex hull. Their predicted decomposition follows five distinct reaction pathways, most commonly into M(III)$_2$Ch$_3$, M(II)X$_2$, and M(II)Ch. Solution processing of six Sn-based MMCHs supports our analysis. Notably, this includes the first synthesis of the previously unreported Sn$_2$InS$_2$Br$_3$ in a multiphase film. Our approach identifies convex hull proximity and competing phase formation as key constraints on MMCH synthetic accessibility during solution processing, thereby guiding future MMCH exploration.